Tungsten ọla kọpa
Nkọwa ngwaahịa
Mkpado ngwaahịa
Ningbo De-Shin awade a zuru nso nke ọla kọpa tungsten (6 ~ 50wt.% Cu) dị iche iche ulo oru ngwa ubi.Ọ na-ewe usoro ntinye oghere oghere dị elu yana ngwaahịa niile na-agbaso ụkpụrụ nke GB/T 8320-2003, ASTM B 702-93 (2004 kwadoro).Tungsten ọla kọpa bụ pseudo-alloy na ọ na-ejide ikike nguzogide tungsten na eletriki eletrik dị elu nke ọla kọpa.
Usoro mmepụta:ntụ ntụ mix -> pịa -> sintering -> agụụ infiltration -> machining -> QC.Usoro mmepụta a niile bụ nke QC na-achịkwa nke ọma iji hụ na arụmọrụ kacha mma.
Uru:
1. Nnukwu arc na-eguzogide jikọtara ya na ezigbo ọkụ eletrik.
2. High thermal conductivity.
3. Mgbasawanye okpomọkụ dị ala.
Ngwa:
1. Arcing kọntaktị na vaccum kọntaktị na elu na ọkara voltaji breakers ma ọ bụ vaccum interruptors.
2. Electrodes na igwe na-egbu ọkụ ọkụ eletrik.
3. Product ngosi!Igwe ọkụ dị ka ihe na-ajụ oyi nke ngwaọrụ eletrọnịkị na ihe nkwakọ ngwaahịa eletrọnịkị.
4. Electrodes maka ịgbado ọkụ na-eguzogide.
Nha ngwaahịa:
mkpanaka tungsten ọla: dayameta≥0.5mm;ogologo ≤300mm.
Tungsten efere ọla kọpa: ọkpụrụkpụ≥1.0mm;ogologo & obosara≤300mm.
| ọkwa | Ngwakọta kemịkalụ (wt%) | Njupụta | Isi ike | Nguzogide | IACS | Na-ehulata Ike | ||
| Cu | Mkpokọta adịghị ọcha≤ | W | g/cm3 ≥ | HB Kgf/mm2 ≥ | μΩ.cm ≤ | % ≥ | MPa ≥ | |
| W50/Cu50 | 50± 2.0 | 0.5 | Nhazi | 11.85 | 115 | 3.2 | 54 | - |
| W55/Cu45 | 45± 2.0 | 0.5 | Nhazi | 12.30 | 125 | 3.5 | 49 | - |
| W60/Cu40 | 40± 2.0 | 0.5 | Nhazi | 12.75 | 140 | 3.7 | 47 | - |
| W65/C35 | 35± 2.0 | 0.5 | Nhazi | 13.30 | 155 | 3.9 | 44 | - |
| W70/C30 | 30± 2.0 | 0.5 | Nhazi | 13.80 | 175 | 4.1 | 42 | 790 |
| W75/Cu25 | 25± 2.0 | 0.5 | Nhazi | 14.50 | 195 | 4.5 | 38 | 885 |
| W80/Cu20 | 20± 2.0 | 0.5 | Nhazi | 15.15 | 220 | 5.0 | 34 | 980 |
| W85/Cu15 | 15± 2.0 | 0.5 | Nhazi | 15.90 | 240 | 5.7 | 30 | 1080 |
| W90/Cu10 | 10± 2.0 | 0.5 | Nhazi | 16.75 | 260 | 6.5 | 27 | 1160 |